Purpose:
Ready-to-use silicate-silicone plaster with a decorative textured effect for use in facade thermal insulation systems based on mineral wool and expanded polystyrene, as well as for interior finishing in dry and wet rooms in buildings and structures.

Substrate type:

• Reinforced base plaster layer.
• Concrete, reinforced concrete, cellular concrete.
• Cement-sand, cement-lime plasters.
• Gypsum plasters.
• Cement putties.
• Sheet gypsum-, cement-, and wood-containing materials.

Application method:

• Manual and mechanized

Consumption:
2.4-2.8 kg/m2

Tinting:
The plaster is produced in the form of a base and can be tinted manually or by computer (machine) method into RAL, NCS, and other color catalogs.

Composition:
Water-based hybrid dispersion of bifunctional copolymers, mineral fillers, innovative additives

Color:
White**

Density:
1.8−1.9 kg/l

Fraction:
1.5 mm

Consumption per 1m2:
2.4-2.8 kg*

Application thickness:
1.5 mm

Drying time to degree 3:
No more than 5 hours***

Resistance to atmospheric precipitation:
Not earlier than 24 hours

Subsequent work:
After 3 days

Shelf life:
24 months

* Material consumption depends on the quality of the substrate preparation, the application method, the tool used, the qualification of the workers, and may differ from the specified values.
** A certain content of particles differing from the main color is allowed, which does not affect the technical characteristics of the product. This is due to the presence of natural fillers in the composition.
*** The stated quality indicators and recommendations are correct for an ambient temperature of +20°C and a relative air humidity of 60%. In other conditions, the drying and adjustment time may differ from those specified.

Purpose and properties
High-quality, ready-to-use plaster based on the most modern solutions for use in facade thermal insulation systems based on mineral wool and expanded polystyrene, as well as for interior finishing in dry and wet rooms in buildings and structures of types A, B, C.
The innovative composition forms a coating with high strength, a self-cleaning effect, and the best ratio of high vapor permeability and low water absorption. Reinforcing microfibers provide the coating with additional strength, elasticity, and resistance to shrinkage.

Technical features
The hybrid nature of the material ensures excellent adhesion and the formation of strong bonds both with the substrate and within the coating itself; vertical bonds facilitate the formation of micro-tunnels for vapor release. The coating is resistant to mold and fungi. It can be tinted in pastel and saturated colors.
The plastic, easy-to-work-with consistency allows for quick and easy application of the plaster to the surface and the formation of the desired texture.

Tinting
Decorative plaster is produced as a base and can be tinted using computer (machine) methods into RAL, NCS, and other color catalogs. Manual tinting is possible using water-based tinting pastes with high light and weather resistance. The organization performing the tinting is responsible for the result.

Color rendering features
Depending on the application conditions and the texture of the surface being painted, actual color shades may differ slightly from those presented in the color catalog.

Before application, it is necessary to perform a test application and check the dried coating for color compliance.
To avoid differences in shade, it is recommended to use a product from the same production batch on a single visual plane (the batch number is indicated on each package) or pre-mix materials from different batches in a 1:1 ratio; the application technology must remain consistent.

Color recommendations
It is recommended to use BERGAUF FACADE GRUNT primer in a color close to the color of the plaster being used.
The use of intense or dark colored materials with a reflection coefficient of less than 25% on facades should be limited to small surfaces occupying no more than 10% of the facade, for example, individual architectural details.

Application technology
Work should be carried out in accordance with SP 293.1325800.2017.
Before application, the plaster must be thoroughly mixed, as product separation may occur during storage. Dilution of the plaster with water is allowed in an amount of no more than 5% of the material weight.
Apply the plaster with a stainless steel trowel at an angle of 60° to the surface; the layer thickness should correspond to the grain size of the plaster. After some time, when the mixture stops sticking to the tool, you can proceed to forming the texture with a plastic trowel. The plastic trowel should be held parallel to the surface, and the texture should be formed with light movements, without pressure.
The "pebble" texture is formed with small circular movements of the float directed in one way, usually counter-clockwise.

Application specifics
If it is necessary to stop work, masking tape is applied along the boundary of the plaster layer, which must be removed before the plaster hardens. To obtain a uniform texture, an adequate number of workers should be ensured at each scaffolding level, and the connection of sections between adjacent levels should be performed using the "wet-on-wet" method.
At ambient temperatures below +20°C and relative air humidity above 60%, the decorative plaster should be protected from direct sunlight, wind, and rain for the first 3 days after application. Under such conditions, it is recommended to cover the scaffolding with a special mesh or film and install water drains on the building. Do not allow freezing or overdrying.
Interior finishing should only be performed in well-ventilated rooms, and after completion of work, air circulation should be maintained until the coating is completely dry.

Subsequent work
The surface of the decorative plaster can be painted with acrylic, silicone, or silicate paints. Painting is carried out no earlier than 3−5 days later, depending on environmental conditions.
Clean tools with water immediately after work. If the tools were not cleaned immediately, they can only be cleaned mechanically later.

Restrictions
It is forbidden to work during precipitation, fog, as well as on wet surfaces after rain and at temperatures below +5 and above +30 °C.

Storage and transportation conditions
Store and transport in tightly closed containers at temperatures of at least +5° and no more than +30°C. Five-fold freezing is allowed for a total duration of no more than 3 weeks at temperatures no lower than -20°C.

The bucket with the product should be protected from excessive heat and storage under direct sunlight should be avoided. Subject to the conditions, the guaranteed shelf life in closed factory packaging is 24 months from the date of manufacture.

Safety
The product is fire and explosion-safe and does not contain flammable components.